A stress level below which the metal will withstand an indefinitely large number of cycles of stress without fracture. When stress is above the fatigue limit, failure occurs by the generation and growth of cracking until fracture results in the remaining structure. If the term is used without qualification, the fatigue limit is usually the number of cycles of stress necessary to produce a complete reverse of flexing stress. See FATIGUE STRESS.